Material Material |
|---|
|
Hardness Hardness |
|---|
|
Density Density |
|---|
|
Flexural Strength Flexural Strength |
|---|
|
Compressive Strength Compressive Strength |
|---|
|
Modulus of Elasticity Modulus of Elasticity |
|---|
|
Thermal Conductivity Thermal Conductivity |
|---|
|
DFARS (Defense Acquisition Regulations Supplement) DFARS (Defense AcquisitionRegulations Supplement)  |
|---|
RoHS (Restriction of Hazardous Substances) RoHS (Restriction ofHazardous Substances) |
|---|
|
REACH (Registration, Evaluation, Authorization and Restriction of Chemicals) REACH (Registration,Evaluation, Authorization and Restriction of Chemicals) |
|---|
|
High-Strength Fracture- and Wear-Resistant Zirconia Ceramic Balls
- Color: White
- Temperature Range: See table
- Fabrication: Sintered
- Porosity: See table
- Compressive Strength: See table
Often used instead of metal in bearings and rollers, these balls are ideal for applications where strength under heavy loads and wear resistance is needed. It's the addition of yttria that gives this zirconia more strength and lowers the chances of cracking from impact than standard zirconia, alumina, and silicon nitride ceramic. If cracks do occur, they will not spread, extending the life and reliability of the material. It also means this zirconia blend resists wearing down from rubbing against another part or abrasion from chemical slurries.
These balls do not withstand rapid temperature changes or high temperatures as well as other high-performance ceramics such as alumina and silicon nitride ceramic.
For technical drawings and 3-D models, click on a part number.
| Diameter | Diameter Tolerance | Minimum Temperature | Maximum Temperature | Compressive Strength, psi | Porosity | Pkg. Qty. | Pkg. | |
| 1/8" | -0.00010" to 0.00010" | -112° F | 2700° F | 350,000 | 13% | 5 | 0000000 | 000000 |
| 3/16" | -0.00010" to 0.00010" | -112° F | 2700° F | 350,000 | 13% | 5 | 0000000 | 00000 |
| 7/32" | -0.00010" to 0.00010" | -112° F | 2700° F | 350,000 | 13% | 5 | 0000000 | 00000 |
| 1/4" | -0.00010" to 0.00010" | -112° F | 2700° F | 350,000 | 13% | 5 | 0000000 | 00000 |
| 3/8" | -0.00010" to 0.00010" | -112° F | 2700° F | 350,000 | 13% | 5 | 0000000 | 00000 |
| 1/2" | -0.05000" to 0.05000" | Not Rated | 1000° F | 300,000 | Not Rated | 1 | 0000000 | 00000 |
| 3/4" | -0.07500" to 0.07500" | Not Rated | 1000° F | 300,000 | Not Rated | 1 | 0000000 | 00000 |
| 1" | -0.10000" to 0.10000" | Not Rated | 1000° F | 300,000 | Not Rated | 1 | 0000000 | 00000 |
| 3mm | -0.00250mm to 0.00250mm | -112° F | 2700° F | 350,000 | 13% | 5 | 0000000 | 00000 |
| 4mm | -0.00250mm to 0.00250mm | -112° F | 2700° F | 350,000 | 13% | 5 | 0000000 | 00000 |
| 5mm | -0.00250mm to 0.00250mm | -112° F | 2700° F | 350,000 | 13% | 5 | 0000000 | 00000 |
| 7mm | -0.00250mm to 0.00250mm | -112° F | 2700° F | 350,000 | 13% | 5 | 0000000 | 00000 |
| 8mm | -0.00250mm to 0.00250mm | -112° F | 2700° F | 350,000 | 13% | 5 | 00000000 | 00000 |
| 10mm | -1.00000mm to 1.00000mm | Not Rated | 1000° F | 300,000 | Not Rated | 5 | 0000000 | 00000 |
| 11mm | -1.10000mm to 1.10000mm | Not Rated | 1000° F | 300,000 | Not Rated | 1 | 000000 | 00000 |
| 12mm | -1.20000mm to 1.20000mm | Not Rated | 1000° F | 300,000 | Not Rated | 1 | 0000000 | 00000 |
| 16mm | -1.60000mm to 1.60000mm | Not Rated | 1000° F | 300,000 | Not Rated | 1 | 0000000 | 00000 |
| 17mm | -1.70000mm to 1.70000mm | Not Rated | 1000° F | 300,000 | Not Rated | 1 | 0000000 | 00000 |
| 25mm | -2.50000mm to 2.50000mm | Not Rated | 1000° F | 300,000 | Not Rated | 1 | 0000000 | 00000 |
Acid-Resistant Silicon-Carbide Ceramic Balls
- Color: Black
- Max. Temperature: 2,550° F
- Fabrication: Sintered
- Porosity: 0.2%
- Compressive Strength: 350,000 psi
Extremely hard with excellent corrosion resistance, this silicon-carbide ceramic is often used for rubbing parts such as bearings and bushings in chemical-processing environments. This material’s hardness means it resists abrasion and wear, but also makes it more brittle than other ceramics. Don’t use it under heavy loads or at high speeds. Nearly chemically inert, it resists corrosion better than other ceramics when in contact with acids and other chemicals. Silicon-carbide ceramic conducts heat well and doesn’t expand significantly from heat, so it won’t deform or crack from temperature swings. Rated for use at up to 2550° F, it’s good for use in furnaces and refractories.
For technical drawings and 3-D models, click on a part number.