System of Measurement System of Measurement |
|---|
|
Diameter Diameter | Show |
|---|
|
Diameter Diameter | Hide |
|---|
Material Material |
|---|
|
|
Appearance Appearance |
|---|
|
Shape Shape |
|---|
 | Ball |
Hardness Hardness |
|---|
|
For Finish For Finish |
|---|
|
Maximum Temperature Maximum Temperature |
|---|
|
Minimum Temperature Minimum Temperature |
|---|
|
Yield Strength Yield Strength |
|---|
|
Heat Treatment Heat Treatment |
|---|
|
For Use On For Use On |
|---|
|
Certificate Certificate |
|---|
 | Material Certificate with Traceable Lot Number |
Specifications Met Specifications Met |
|---|
|
Weight Weight |
|---|
|
Density Density |
|---|
|
Fabrication Fabrication |
|---|
|
Recommended Media to Parts Ratio RecommendedMedia to Parts Ratio |
|---|
|
Aluminum Performance Properties Aluminum PerformanceProperties |
|---|
|
Construction Construction |
|---|
|
About Stainless Steel
More
About Aluminum
More
About Carbon Steel, Alloy Steel, Spring Steel, and Cast Iron
More
Hardened Bearing-Quality 440C Stainless Steel
- Yield Strength: Not Rated
- Hardness: Rockwell C60 (Very Hard)
- Heat Treatment: Hardened
- Specifications Met: SAE AMS5630
These balls are hardened for increased wear and abrasion resistance. 440C is one of the hardest types of stainless steel after heat treating. It's often used for bearings and valves. This material maintains its corrosion resistance in temperatures up to 800° F.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ACTIVITY after your order ships.
| Dia. | Dia. Tolerance | Magnetic Properties | Pkg. Qty. | Pkg. | |
Mirror-Like | |||||
|---|---|---|---|---|---|
| 1mm | -0.0025mm to 0.0025mm | Magnetic | 250 | 0000000 | 000000 |
Hard Wear-Resistant 52100 Alloy Steel Balls
- Yield Strength: 295,000 psi
- Hardness: Rockwell C60 (Very Hard)
- Specifications Met: See table
Also known as chrome steel, 52100 is an extremely hard and wear-resistant material. These balls are often used in bearings.
For technical drawings and 3-D models, click on a part number.
| Dia. | Dia. Tolerance | Heat Treatment | Pkg. Qty. | Pkg. | |
Mirror-Like | |||||
|---|---|---|---|---|---|
| 1mm | -0.0025mm to 0.0025mm | Hardened | 100 | 0000000 | 00000 |
Ultra-Hard C2 Tungsten Carbide Balls
- Yield Strength: Not Rated
- Hardness: Rockwell C75 (Very Hard)
- Temper Rating: Not Rated
Tungsten carbide, sometimes called carbide, is harder than Corrosion-Resistant Tungsten with excellent wear resistance. Use it to machine long-lasting tools, such as end mills and inserts.
For technical drawings and 3-D models, click on a part number.
| Dia. | Dia. Tolerance | Mechanical Finish | Pkg. Qty. | Pkg. | |
| 1mm | -0.0025mm to 0.0025mm | Polished | 5 | 0000000 | 000000 |
2017 Aluminum
- Yield Strength: 32,000 psi
- Hardness: Brinell 110 (Soft)
- Temper: T4
Widely used as bearings and in valves, these 2017 aluminum balls are durable and lightweight.
For technical drawings and 3-D models, click on a part number.
| Dia. | Dia. Tolerance | Heat Treatment | Pkg. Qty. | Pkg. | |
| 1mm | -0.025mm to 0.025mm | Hardened | 100 | 00000000 | 000000 |
Mirror-Finish Polishing Media for Steel,
Stainless Steel, and Hard Metals
Often used as the final step after other media, this type of media is also good for use on fragile parts and won't contaminate nonferrous materials. Choose a size that’s large enough not to lodge in recesses and holes. Use with liquid compounds in tumbling and vibrating machines.
5 lbs. | ||||||
|---|---|---|---|---|---|---|
| Dia., mm | Density, lbs./cu. ft. | Recommended Media to Parts Ratio | For Finish | Material | Pkg. | |
Ball | ||||||
| 1 | 125 | 3:1 | Mirror | Porcelain | 0000000 | 000000 |