Container Type Container Type |
---|
![]() | Cartridge |
For Use On For Use On |
---|
Manufacturer Manufacturer |
---|
|
Manufacturer Model Number ManufacturerModel Number | Show |
---|
|
Manufacturer Model Number ManufacturerModel Number | Hide |
---|
Formulation Formulation |
---|
|
Begins to Harden Begins to Harden |
---|
|
Type Type |
---|
|
Adhesive Type Adhesive Type |
---|
|
Reaches Full Strength Reaches Full Strength |
---|
|
Color Color |
---|
![]() | Off-White |
Mix Ratio Mix Ratio |
---|
|
Consistency Consistency |
---|
|
Cure Type Cure Type |
---|
|
Maximum Temperature Maximum Temperature |
---|
|
Minimum Temperature Minimum Temperature |
---|
|
Approximate Coverage Approximate Coverage |
---|
|
Viscosity Viscosity |
---|
|
Peel Strength Peel Strength |
---|
|
Mixing Required Mixing Required |
---|
|
Clarity Clarity |
---|
|
Connection Type Connection Type |
---|
|
More
Toughened adhesives are blended with rubber particles for better impact resistance than standard epoxies. They form flexible, resilient bonds. The most weather- and chemical-resistant structural adhesives, epoxies work especially well on metals. Choose an adhesive that hardens quickly for fast repairs, or one that hardens slowly to allow more time for positioning.
The size listed is the combined total of the two parts. Use with a dispensing gun and mixer nozzle to simultaneously mix and dispense adhesives.
Container | Strength | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Shear, lbs./sq. in. | Peel, lbs./in. wd. | Mix Ratio | Consistency (Viscosity) | Temp. Range, °F | Color | For Joining | Each | |
E-20HP | 1.69 | Cartridge | 20 min. | 24 hrs. | 3,270 | Not Rated | 2:1 | Thick Liquid (30,000 cP) | -65° to 250° | Off-White | Metal, Plastic, Rubber | 0000000 | 000000 |
E-20HP | 6.76 | Cartridge | 20 min. | 24 hrs. | 3,270 | Not Rated | 2:1 | Thick Liquid (30,000 cP) | -65° to 250° | Off-White | Metal, Plastic, Rubber | 0000000 | 00000 |