Color Color |
---|
For Joining For Joining |
---|
For Use On For Use On | Show |
---|
|
For Use On For Use On | Hide |
---|
Formulation Formulation |
---|
|
Maximum Temperature Maximum Temperature |
---|
|
Container Size Container Size |
---|
Reaches Full Strength Reaches Full Strength |
---|
|
|
Manufacturer Manufacturer |
---|
|
|
Begins to Harden Begins to Harden |
---|
|
|
|
Specifications Met Specifications Met |
---|
|
Clarity Clarity |
---|
|
Application Application |
---|
|
Minimum Temperature Minimum Temperature |
---|
|
Hardness Rating Hardness Rating |
---|
Manufacturer Model Number Manufacturer Model Number |
---|
Tensile Strength Tensile Strength |
---|
|
For Use With For Use With |
---|
|
More
More
Mix these two-part epoxy surface fillers to create a strong repair in wet environments or underwater. Use them to repair cracked, worn, and damaged surfaces. Size listed is the combined total of the two parts.
Paste fillers resist alkalies, solvents, gasoline, and oil.
Container | ||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden, min. | Reaches Full Strength | Consistency | Mix Ratio | Approx. Coverage @ Thick. | Max. Thick. | For Use Outdoors | Temp. Range, °F | Color | Finishing Method | For Use On | Each | |
Surface Fillers | ||||||||||||||
2 | Tube | 5 | 24 hrs. | Paste | 1:1 | 12 sq. in. @ 1/4" | 1/2" | Yes | Not Rated to 200° | Gray | Machine, Drill, Sand, Saw, Tap | Aluminum, Brass, Bronze, Copper, Steel, Galvanized Iron, Galvanized Steel, Titanium, Acrylic Plastic, ABS Plastic, PVC Plastic, CPVC Plastic, Polyimide Plastic, Nylon Plastic, Vinyl Plastic, EPDM Rubber, Fiberglass, Glass, Concrete, Ceramic, Porcelain, Plaster, Grout, Masonry, Asphalt, Stone, Wood | 0000000 | 000000 |
2 | Jar, Bottle | 20 | 60 min. | Paste | 5:1 | 8 1/2 sq. in. @ 1/4" | 1 1/2" | Yes | Not Rated to 185° | White | Machine, Drill, Sand, Saw, Tap | Aluminum, Brass, Bronze, Copper, Steel, Galvanized Iron, Galvanized Steel, Titanium, Acrylic Plastic, ABS Plastic, PVC Plastic, CPVC Plastic, Polyimide Plastic, Nylon Plastic, Vinyl Plastic, EPDM Rubber, Fiberglass, Glass, Concrete, Ceramic, Porcelain, Plaster, Grout, Masonry, Asphalt, Stone, Wood | 0000000 | 00000 |
2 | Jar, Bottle | 20 | 60 min. | Paste | 5:1 | 8 1/2 sq. in. @ 1/4" | 1 1/2" | Yes | Not Rated to 250° | Gray | Machine, Drill, Sand, Saw, Tap | Aluminum, Brass, Bronze, Copper, Steel, Galvanized Iron, Galvanized Steel, Titanium, Acrylic Plastic, ABS Plastic, PVC Plastic, CPVC Plastic, Polyimide Plastic, Nylon Plastic, Vinyl Plastic, EPDM Rubber, Fiberglass, Glass, Concrete, Ceramic, Porcelain, Plaster, Grout, Masonry, Asphalt, Stone, Wood | 0000000 | 00000 |
14 | Can, Jar | 20 | 60 min. | Paste | 5:1 | 62 sq. in. @ 1/4" | 1 1/2" | Yes | Not Rated to 185° | White | Machine, Drill, Sand, Saw, Tap | Aluminum, Brass, Bronze, Copper, Steel, Galvanized Iron, Galvanized Steel, Titanium, Acrylic Plastic, ABS Plastic, PVC Plastic, CPVC Plastic, Polyimide Plastic, Nylon Plastic, Vinyl Plastic, EPDM Rubber, Fiberglass, Glass, Concrete, Ceramic, Porcelain, Plaster, Grout, Masonry, Asphalt, Stone, Wood | 0000000 | 00000 |
14 | Can, Jar | 20 | 60 min. | Paste | 5:1 | 62 sq. in. @ 1/4" | 1 1/2" | Yes | Not Rated to 250° | Gray | Machine, Drill, Sand, Saw, Tap | Aluminum, Brass, Bronze, Copper, Steel, Galvanized Iron, Galvanized Steel, Titanium, Acrylic Plastic, ABS Plastic, PVC Plastic, CPVC Plastic, Polyimide Plastic, Nylon Plastic, Vinyl Plastic, EPDM Rubber, Fiberglass, Glass, Concrete, Ceramic, Porcelain, Plaster, Grout, Masonry, Asphalt, Stone, Wood | 0000000 | 00000 |
Also known as sloshing compounds, these two-part epoxies bond to rough and rusty surfaces in fuel tanks to repair leaks and prevent further corrosion. They withstand permanent immersion in fuel, oil, and harsh solvents. Use them with metal, plastic, and fiberglass tanks. Mix the smaller can with the bigger one and pour into your fuel tank. Rotate the tank to coat the interior and dump out any excess. Allow to cure overnight. Size listed is the combined total of the two parts.
1.5-pint container can treat a 10-gallon fuel tank. 3-pint container can treat a 20-gallon fuel tank.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, pt. | Type | Begins to Harden, min. | Reaches Full Strength, hrs. | Consistency | Mix Ratio | For Use Outdoors | Temp. Range, °F | Color | Finishing Method | For Use On | Each | |
1.5 | Can | 5 | 24 | Thick Liquid | 2:1 | No | 70° to 90° | Amber | Drill, Sand, Tap | Aluminum, Brass, Bronze, Copper, Silver, Steel, Stainless Steel, Cast Iron, Galvanized Iron, Galvanized Steel, Titanium, Acrylic Plastic, Polycarbonate Plastic, ABS Plastic, PVC Plastic, CPVC Plastic, PETG Plastic, PVDF Plastic, Polyimide Plastic, Nylon Plastic, Polyethylene Plastic, Polypropylene Plastic, Vinyl Plastic, Fiberglass, Ceramic, Porcelain | 0000000 | 000000 |
3 | Can | 5 | 24 | Thick Liquid | 2:1 | No | 70° to 90° | Amber | Drill, Sand, Tap | Aluminum, Brass, Bronze, Copper, Silver, Steel, Stainless Steel, Cast Iron, Galvanized Iron, Galvanized Steel, Titanium, Acrylic Plastic, Polycarbonate Plastic, ABS Plastic, PVC Plastic, CPVC Plastic, PETG Plastic, PVDF Plastic, Polyimide Plastic, Nylon Plastic, Polyethylene Plastic, Polypropylene Plastic, Vinyl Plastic, Fiberglass, Ceramic, Porcelain | 0000000 | 00000 |
Repair small leaks and cracks in coolant systems for commercial vehicles and industrial equipment. These surface fillers meet ASTM D3147 for their ability to stop leaks in engine cooling systems. Pour them into your coolant to fix both internal and external leaks. They contain ceramic microfibers and copper particles to create a permanent seal. They’re compatible with antifreeze and other coolant system additives.
Container | |||||||||
---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden, min. | Reaches Full Strength, min. | Consistency | Temp. Range, °F | Color | For Use On | Each | |
16 | Jug | 7 | 10 | Thick Liquid | Not Rated to 500° | Brown | Aluminum, Brass, Bronze, Copper, Silver, Steel, Stainless Steel, Galvanized Steel, Galvanized Iron, Titanium, Acrylic Plastic, Polystyrene Plastic, Polycarbonate Plastic, ABS Plastic, PVC Plastic, CPVC Plastic, PETG Plastic, PVDF Plastic, Polyimide Plastic, Nylon Plastic, PTFE Plastic, Polyethylene Plastic, Polypropylene Plastic | 0000000 | 000000 |
Made from silicone, these sealants are RTV (room-temperature vulcanizing). They’re non-sagging, so they won't drip from vertical and overhead surfaces.
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. Sealants that are good for joining dissimilar materials also work well in environments with wide temperature fluctuation.
When Dow Corning 700 requires a primer, for best results use PR-1200 on metal and PR-1205 on plastic.
Container | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Temp. Range, °F | For Joining | Specifications Met | Choose a Color | Each | |
Dow Corning Silicone | |||||||||||||
700 | 3 | Tube | 15 min. | 24 hrs. | 575% | -25% to 25% | Soft (Durometer 20A) | -75° to 350° | Metal Metal to Plastic Metal to Rubber Metal to Glass Plastic Plastic to Rubber Plastic to Glass Rubber Rubber to Glass Glass | FDA Compliant 21 CFR 177.2600, NSF/ANSI 51, UL Recognized Component | Clear | 0000000 | 00000 |
700 | 10.1 | Cartridge | 15 min. | 24 hrs. | 575% | -25% to 25% | Soft (Durometer 20A) | -75° to 350° | Metal Metal to Plastic Metal to Rubber Metal to Glass Plastic Plastic to Rubber Plastic to Glass Rubber Rubber to Glass Glass | FDA Compliant 21 CFR 177.2600, NSF/ANSI 51, UL Recognized Component | 000000 | 0000 | |
706 | 10.1 | Cartridge | 25 min. | 24 hrs. | 350% | -25% to 25% | Soft (Durometer 20A) | -60° to 500° | Metal Metal to Plastic Metal to Glass Plastic Glass | FDA Compliant 21 CFR 177.2600, MIL-A-46106B Group I Type I, UL Recognized Component | Red | 0000000 | 0000 |
732 | 3 | Tube | 20 min. | 24 hrs. | 600% | -25% to 25% | Soft (Durometer 25A) | -75° to 350° | Metal Metal to Plastic Metal to Glass Plastic Glass | FDA Compliant 21 CFR 177.2600, MIL-A-46106B Group I Type I, NSF/ANSI 51, NSF/ANSI 61, UL Listed | 000000 | 0000 | |
732 | 10.1 | Cartridge | 20 min. | 24 hrs. | 600% | -25% to 25% | Soft (Durometer 25A) | -75° to 350° | Metal Metal to Plastic Metal to Glass Plastic Glass | FDA Compliant 21 CFR 177.2600, MIL-A-46106B Group I Type I, NSF/ANSI 51, NSF/ANSI 61, UL Listed | 000000 | 0000 | |
Silicone | |||||||||||||
__ | 9.8 | Cartridge | 5 min. | 24 hrs. | Not Rated | -25% to 25% | Not Rated | -40° to 350° | Metal Metal to Plastic Metal to Glass Plastic Plastic to Glass Glass | ASTM C920 Type S Grade NS Class 25, FDA Compliant 21 CFR 177.2600 | 000000 | 0000 |
Resistant to mold and mildew, these sealants are well suited to high-humidity environments. They’re non-sagging, so they won't drip from vertical and overhead surfaces. Made from silicone, sealants are RTV (room-temperature vulcanizing).
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. Sealants that are good for joining dissimilar materials also work well in environments with wide temperature fluctuation.
Dow Corning 786 meets NSF/ANSI 51 standards and is FDA compliant for direct contact with food.
Container | ||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Temp. Range, °F | For Joining | Specifications Met | Color | Clarity | Each | |
Dow Corning Silicone | ||||||||||||||
786 | 10.1 | Cartridge | 20 min. | 48 hrs. | 600% | -25% to 25% | Soft (Durometer 25A) | -75° to 350° | Metal Metal to Plastic Plastic Masonry | ASTM C920 Type S Grade NS Class 25, FDA Compliant 21 CFR 177.2600, NSF/ANSI 51 | White | Opaque | 00000000 | 00000 |
786 | 10.1 | Cartridge | 20 min. | 48 hrs. | 600% | -25% to 25% | Soft (Durometer 25A) | -75° to 350° | Metal Metal to Plastic Plastic Masonry | ASTM C920 Type S Grade NS Class 25, FDA Compliant 21 CFR 177.2600, NSF/ANSI 51 | White | Semi-Clear | 00000000 | 0000 |
Primer for Dow Corning Sealants (16-oz. Bottle) | 0000000 | Each | 000000 |
Thinner than non-sagging sealants, these flow easily into cracks and have a smooth finish. Made from silicone, sealants are RTV (room-temperature vulcanizing).
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. Sealants that are good for joining dissimilar materials also work well in environments with wide temperature fluctuation.
Container | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Tensile Strength, psi | Hardness | Temp. Range, °F | For Joining | Choose a Color | Each | |
Dow Corning Silicone | |||||||||||||
734 | 3 | Tube | 15 min. | 24 hrs. | 315% | -25% to 25% | 215 | Soft (Durometer 27A) | -85° to 350° | Metal Metal to Plastic Metal to Rubber Metal to Glass Plastic Plastic to Rubber Plastic to Glass Rubber Rubber to Glass Glass | 0000000 | 000000 | |
734 | 10.1 | Cartridge | 15 min. | 24 hrs. | 315% | -25% to 25% | 215 | Soft (Durometer 27A) | -85° to 350° | Metal Metal to Plastic Metal to Rubber Metal to Glass Plastic Plastic to Rubber Plastic to Glass Rubber Rubber to Glass Glass | 0000000 | 00000 |
Primer for Dow Corning and Loctite® Sealants (16-oz. Bottle) | 0000000 | Each | 000000 |
Also known as neutral-cure sealants, these won't discolor copper, brass, and concrete. They’re non-sagging, so they won't drip from vertical and overhead surfaces. Made from silicone, sealants are RTV (room-temperature vulcanizing).
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. Sealants that are good for joining dissimilar materials also work well in environments with wide temperature fluctuation.
Sealants that cannot be sold to California exceed local regulatory limits on VOCs (volatile organic compounds).
Container | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Temp. Range, °F | For Joining | Cannot Be Sold To | Choose a Color | Each | |
Dow Corning Silicone | |||||||||||||
739 | 10.1 | Cartridge | 5 min. | 24 hrs. | 640% | -25% to 25% | Soft (Durometer 37A) | -65° to 300° | Metal Metal to Plastic Metal to Rubber Metal to Glass Plastic Plastic to Rubber Plastic to Glass Rubber Rubber to Glass Glass | __ | 0000000 | 000000 | |
832 | 10.1 | Cartridge | 50 min. | 24 hrs. | 420% | -25% to 25% | Soft (Durometer 35A) | -65° to 300° | Metal Metal to Plastic Metal to Glass Plastic Plastic to Glass Glass Masonry | __ | 0000000 | 00000 | |
Loctite® Silicone | |||||||||||||
SI 5011 CL | 2.7 | Tube | 20 min. | 24 hrs. | 300% | Not Rated | Soft (Durometer 20A) | -75° to 400° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood | __ | Clear | 0000000 | 00000 |
SI 5011 CL | 10.1 | Cartridge | 20 min. | 24 hrs. | 300% | Not Rated | Soft (Durometer 20A) | -75° to 400° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood | __ | Clear | 0000000 | 00000 |
SI 5109 | 10.1 | Cartridge | 60 min. | 24 hrs. | 300% | Not Rated | Soft (Durometer 18A) | -75° to 600° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood | __ | Red | 0000000 | 00000 |
Permatex Silicone | |||||||||||||
81173 | 12.9 | Cartridge | 30 min. | 24 hrs. | 350% | Not Rated | Soft (Durometer 18A) | -75° to 450° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood | CA | Black | 0000000 | 00000 |
Primer for Dow Corning 737, 739, and 790 Sealants (16-oz. Bottle) | 0000000 | Each | 000000 |
Form seals that resist punctures, cuts, and abrasion to withstand heavy wear and tampering. These sealants are non-sagging, so they won't drip from vertical and overhead surfaces.
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. These sealants are best suited to joints between similar materials that aren't exposed to wide temperature fluctuation.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Tensile Strength, psi | Hardness | Temp. Range, °F | For Joining | Color | Each | |
Polyurethane | ||||||||||||
10.1 | Cartridge | 90 min. | 48 hrs. | 225% | -12.5% to 12.5% | 250 | Medium (Durometer 55A) | 20° to 120° | Metal, Plastic, Rubber, Asphalt, Composites, Glass, Masonry, Wood | White | 0000000 | 000000 |
20 | Sausage Pack | 90 min. | 48 hrs. | 225% | -12.5% to 12.5% | 250 | Medium (Durometer 55A) | 20° to 120° | Metal, Plastic, Rubber, Asphalt, Composites, Glass, Masonry, Wood | White | 0000000 | 00000 |
These structural sealants combine the mechanical strength of an adhesive with excellent sealing properties and high flexibility. They’re non-sagging, so they won't drip from vertical and overhead surfaces.
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. For joints between dissimilar materials and in environments with wide temperature fluctuation, choose a sealant with a higher elongation or joint compression/expansion tolerance. For high-wear applications, choose a harder sealant for the most abrasion resistance.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Temp. Range, °F | For Joining | Choose a Color | Each | |
3M Hybrid Polymer | ||||||||||||
760 UV | 9.8 | Cartridge | 30 min. | 24 hrs. | 100% | Not Rated | Medium Hard (Durometer 55A) | -40° to 212° | Metal Metal to Plastic Metal to Rubber Metal to Composites Plastic Plastic to Rubber Plastic to Composites Rubber Rubber to Composites Composites Wood | 00000000 | 000000 | |
760 UV | 20.3 | Sausage Pack | 30 min. | 24 hrs. | 100% | Not Rated | Medium Hard (Durometer 55A) | -40° to 212° | Metal Metal to Plastic Metal to Rubber Metal to Composites Plastic Plastic to Rubber Plastic to Composites Rubber Rubber to Composites Composites Wood | 00000000 | 00000 | |
3M Polyurethane | ||||||||||||
540 | 20.3 | Sausage Pack | 90 min. | 24 hrs. | 600% | -25% to 25% | Medium Soft (Durometer 40A) | -40° to 190° | Metal Plastic Rubber Composites Wood | 00000000 | 00000 | |
551 | 20.3 | Sausage Pack | 180 min. | 24 hrs. | 600% | Not Rated | Medium (Durometer 45A) | -40° to 190° | Metal Metal to Plastic Metal to Rubber Metal to Composites Plastic Plastic to Rubber Plastic to Composites Rubber Rubber to Composites Composites Wood | White | 00000000 | 00000 |
560 | 20.3 | Sausage Pack | 60 min. | 24 hrs. | 300% | Not Rated | Medium Hard (Durometer 55A) | -40° to 190° | Metal Metal to Plastic Metal to Rubber Metal to Composites Plastic Plastic to Rubber Plastic to Composites Rubber Rubber to Composites Composites Wood | 00000000 | 00000 |
![]() | ![]() | ![]() | ||||
![]() | ![]() | ![]() White | ||||
![]() Bronze | ![]() Limestone | ![]() Tan | ![]() Black | ![]() Gray |
Apply these sealants in cold temperatures, on wet surfaces, and even through running water. They are structural sealants that combine the mechanical strength of an adhesive with excellent sealing properties and high flexibility. Sealants are non-sagging, so they won't drip from vertical and overhead surfaces.
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. These sealants are good for use between dissimilar materials and in environments with wide temperature fluctuation.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Size | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Tensile Strength, psi | Hardness | Temp. Range, °F | For Joining | Choose a Color | Each | |
Polyether | ||||||||||||
5 oz. | Tube | 20 min. | 7 days | 525% | -35% to 35% | 370 | Medium (Durometer 45A) | -40° to 200° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood Wood to Glass | White | 000000 | 00000 |
10.1 oz. | Cartridge | 20 min. | 7 days | 525% | -35% to 35% | 370 | Medium (Durometer 45A) | -40° to 200° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood Wood to Glass | 0000000 | 0000 | |
20 oz. | Sausage Pack | 20 min. | 7 days | 525% | -35% to 35% | 370 | Medium (Durometer 45A) | -40° to 200° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood Wood to Glass | 000000 | 00000 | |
28 oz. | Cartridge | 20 min. | 7 days | 525% | -35% to 35% | 370 | Medium (Durometer 45A) | -40° to 200° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood Wood to Glass | 000000 | 00000 | |
2 gal. | Pail | 20 min. | 7 days | 525% | -35% to 35% | 370 | Medium (Durometer 45A) | -40° to 200° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood Wood to Glass | 000000 | 000000 | |
5 gal. | Pail | 20 min. | 7 days | 525% | -35% to 35% | 370 | Medium (Durometer 45A) | -40° to 200° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood Wood to Glass | 000000 | 000000 |
These non-sagging sealants will not drip while hardening on vertical and overhead surfaces. They’re marine grade, so they stand up to water, corrosion from salt spray, mildew, and UV light.
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. Sealants that are good for joining dissimilar materials also work well in environments with wide temperature fluctuation.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Temp. Range, °F | For Joining | Choose a Color | Each | |
3M Hybrid Polymer | ||||||||||||
4000UV | 20.3 | Sausage Pack | 30 min. | 24 hrs. | 700% | Not Rated | Medium Soft (Durometer 40A) | -40° to 190° | Metal Metal to Plastic Metal to Composites Plastic Plastic to Composites Composites Wood | White | 00000000 | 000000 |
3M Polyurethane | ||||||||||||
4200 FC | 3 | Tube | 2 hrs. | 24 hrs. | 400% | Not Rated | Medium Soft (Durometer 40A) | -40° to 190° | Metal Metal to Plastic Metal to Composites Metal to Glass Plastic Plastic to Composites Plastic to Glass Composites Glass Wood Wood to Glass | White | 00000000 | 00000 |
4200 FC | 10 | Cartridge | 2 hrs. | 24 hrs. | 400% | Not Rated | Medium Soft (Durometer 40A) | -40° to 190° | Metal Metal to Plastic Metal to Composites Metal to Glass Plastic Plastic to Composites Plastic to Glass Composites Glass Wood Wood to Glass | 00000000 | 00000 |
Thinner than non-sagging sealants, these flow easily into cracks and have a smooth finish.
Elongation and joint expansion/compression tolerance indicate flexibility. For joints between dissimilar materials and in environments with wide temperature fluctuation, choose a sealant with a higher elongation or joint expansion/compression tolerance. For high-wear applications, choose a harder sealant for the most abrasion resistance.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Tensile Strength, psi | Hardness | Temp. Range, °F | For Joining | Choose a Color | Each | |
Buna-N | ||||||||||||
4 | Tube | 10 min. | 24 hrs. | 1,000% | Not Rated | Not Rated | Soft (Durometer 25A) | -30° to 300° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood | 0000000 | 00000 | |
10.3 | Cartridge | 10 min. | 24 hrs. | 600% | Not Rated | Not Rated | Soft (Durometer 30A) | -30° to 300° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Asphalt Composites Composites to Glass Glass Masonry Wood | 0000000 | 0000 | |
Thermoplastic | ||||||||||||
2 | Tube | 3 min. | 3 hrs. | 25% | -2% to 2% | 7,250 | Extra Hard (Durometer 90A) | -40° to 150° | Metal Plastic Rubber Asphalt Composites Glass Masonry Wood | Clear | 0000000 | 0000 |
These non-sagging sealants will not drip while hardening on vertical and overhead surfaces. They’re thicker than most non-sagging sealants, so they can be used in vertical joints up to 1/2" wide.
Elongation indicates flexibility—the higher the values are, the more sealants can stretch. These sealants are best suited to joints between similar materials that aren't exposed to wide temperature fluctuation.
Container | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Tensile Strength | Hardness | Temp. Range, °F | For Joining | Color | Each | |
Buna-N | |||||||||||
10.3 | Cartridge | 10 min. | 24 hrs. | 100% | Not Rated | Soft (Durometer 20A) | -30° to 300° | Metal, Plastic, Rubber, Composites, Glass, Masonry, Wood | Aluminum | 0000000 | 000000 |
Seal joints and gaps in concrete. These sealants are non-sagging, so they won't drip from vertical and overhead surfaces.
Silicone sealant is RTV (room-temperature vulcanizing).
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. These sealants are best suited to joints between similar materials that aren't exposed to wide temperature fluctuation.
Container | For Max. Crack | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Wd. | Dp. | Application Temp. Range, °F | Temp. Range, °F | For Joining | Color | Each | |
Silicone | ||||||||||||||
10.1 | Cartridge | 15 min. | 24 hrs. | Not Rated | -25% to 25% | Not Rated | 3/8" | 3/8" | 40° to 120° | -40° to 300° | Plastic, Rubber, Masonry, Wood | Gray | 000000 | 00000 |
Seal concrete joints in high-traffic areas—these sealants stand up to heavy wear and tear, such as steel wheel traffic. They're non-sagging, so they won't drip from vertical and overhead surfaces. Made from silicone, sealants are RTV (room-temperature vulcanizing).
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. These sealants are best suited to joints between similar materials that aren't exposed to wide temperature fluctuation. For high-wear applications, choose a harder sealant for the most abrasion resistance.
Container | For Max. Crack | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Wd. | Dp. | Temp. Range, °F | For Joining | Color | For Joining | Each | |
Silicone | ||||||||||||||
20 | Sausage Pack | 60 min. | 7 days | 1,000% | -50% to 100% | Medium Hard (Durometer 55A) | 1" | 1/2" | -20° to 300° | Metal, Plastic, Rubber, Composites, Glass, Masonry, Wood | Gray | Composites, Glass, Masonry, Metal, Plastic, Rubber, Wood | 000000 | 000000 |
29 | Cartridge | 60 min. | 7 days | 1,000% | -50% to 100% | Medium Hard (Durometer 55A) | 1" | 1/2" | -20° to 300° | Metal, Plastic, Rubber, Composites, Glass, Masonry, Wood | Gray | Composites, Glass, Masonry, Metal, Plastic, Rubber, Wood | 000000 | 00000 |
Seal concrete joints in high-traffic locations—these sealants stand up to heavy wear and tear, such as steel wheel traffic. Thinner than non-sagging sealants, these flow easily into cracks and have a smooth finish.
Silicone sealant is RTV (room-temperature vulcanizing).
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. These sealants are best suited to joints between similar materials that aren't exposed to wide temperature fluctuation. For high-wear applications, choose a harder sealant for the most abrasion resistance.
Container | For Max. Crack | ||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Mix Ratio | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Wd. | Dp. | Temp. Range, °F | For Joining | Color | Each | |
Loctite® Polyurethane | |||||||||||||||
PC 6231 | 8.6 | Cartridge | 3 min. | 90 min. | 1:1 | 82% | -10% to 10% | Hard (Durometer 75A) | 3/4" | 2 1/4" | -40° to 120° | Metal, Plastic, Rubber, Asphalt, Composites, Glass, Masonry, Wood | Gray | 0000000 | 000000 |
Silicone | |||||||||||||||
__ | 29 | Cartridge | 60 min. | 7 days | __ | 1,000% | -50% to 100% | Soft (Durometer 20A) | 1" | 1/2" | -60° to 300° | Metal, Plastic, Rubber, Composites, Glass, Masonry, Wood | Limestone | 0000000 | 00000 |
Often used in high-vibration applications that could cause standard thread sealants to fail, these never fully harden and remain pliable enough to self-heal and stop leaks before they start. They have low locking strength, so they can be adjusted without tools.
To adhere to safety standards for drinking water systems, use sealants that meet NSF/ANSI 61.
Sealants that cannot be sold to the regions listed exceed local regulatory limits on VOCs (volatile organic compounds).
Container | Max. Pressure, psi | |||||||||
---|---|---|---|---|---|---|---|---|---|---|
Size | Type | For Fluids | For Gases | Temp. Range, °F | Consistency | Specifications Met | Color | Cannot Be Sold To | Each | |
Low Locking Strength | ||||||||||
Sealants | ||||||||||
8 oz. | Brush-Top Can | 6,000 | 3,000 | 20° to 140° | Paste | NSF/ANSI 61 | Blue | CT, DC, DE, IL, IN, MA, MD, ME, MI, NH, NJ, NY, OH, PA, RI, UT, Northern VA | 000000 | 000000 |
Keep out the elements by sealing roof joints. These sealants are non-sagging, so they won't drip from vertical and overhead surfaces. They are good for use in environments with wide temperature fluctuation.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Tensile Strength, psi | Hardness | Temp. Range, °F | For Joining | Color | Each | |
Butyl Rubber | ||||||||||||
10.1 | Cartridge | 24 hrs. | 48 hrs. | Not Rated | Not Rated | Not Rated | Not Rated | -40° to 180° | Metal, Plastic, Rubber, Masonry, Wood | White | 0000000 | 00000 |
These sealants don't degrade in sunlight. Also known as glazing compounds, use these sealants to install glass in framing. They’re non-sagging, so they won't drip from vertical and overhead surfaces. Made from silicone, these sealants are RTV (room-temperature vulcanizing).
Elongation and joint compression/expansion tolerance indicate flexibility. For joints between dissimilar materials and in environments with wide temperature fluctuation, choose a sealant with a higher elongation or joint compression/expansion tolerance.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Temp. Range, °F | Specifications Met | For Joining | Choose a Color | Each | |
Silicone | ||||||||||||
10.1 | Cartridge | 30 min. | 24 hrs. | 475% | -25% to 25% | Soft (Durometer 20A) | -75° to 400° | FDA Compliant 21 CFR 175.105, FDA Compliant 21 CFR 177.2600, Fed. Spec. TT-S-001543A Type II Class A, Fed. Spec. TT-S-00230C Type II Class A, NSF/ANSI 51 | Metal Metal to Glass Plastic Plastic to Glass Rubber Rubber to Glass Composites Composites to Glass Glass Masonry Wood Wood to Glass | 0000000 | 00000 |
For quick repairs, these epoxies begin to harden in 6 minutes or less. Epoxies are the strongest and most weather- and chemical-resistant structural adhesives.
The size listed is the combined total of the two parts. Use cartridges with a dispensing gun and mixer nozzle to simultaneously mix and dispense adhesives.
HY4090 is a blend of epoxy and instant-bond adhesive for a balance of strength, cure speed, and temperature resistance.
50132 works especially well on plastics and composites.
Container | Strength | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Shear, lbs./sq. in. | Peel | Mix Ratio | Consistency (Viscosity) | Temp. Range, °F | Color | For Joining | Each | |
HY4090 | 1.69 | Cartridge | 3 min. | 7 days | 2,420 | Not Rated | 1:1 | Thick Liquid (19,000 cP) | -65° to 300° | Gray | Metal, Plastic, Rubber, Composites, Masonry, Wood | 00000000 | 000000 |
HY4090 | 1.69 | Cartridge | 3 min. | 7 days | 2,420 | Not Rated | 1:1 | Thick Liquid (19,000 cP) | -65° to 300° | Off-White | Metal, Plastic, Rubber, Composites, Masonry, Wood | 00000000 | 00000 |
HY4090 | 13.5 | Cartridge | 3 min. | 7 days | 2,420 | Not Rated | 1:1 | Thick Liquid (19,000 cP) | -65° to 300° | Off-White | Metal, Plastic, Rubber, Composites, Masonry, Wood | 0000000 | 000000 |
Mfr. Model | Container | Strength | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Name | No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Shear, lbs./sq. in. | Peel | Mix Ratio | Consistency (Viscosity) | Temp. Range, °F | Color | For Joining | Each | |
PlasticWeld | 50132 | 0.85 | Syringe | 5 min. | 60 min. | 2,000 | Not Rated | 1:1 | Thick Liquid (9,000 cP) | -20° to 300° | Off-White | Metal, Plastic, Rubber, Composites, Masonry, Wood | 000000 | 00000 |
Epoxies are the strongest and most weather- and chemical-resistant structural adhesives. They work especially well on metals. For putty adhesives, slice off the required amount, then knead it together to form a moldable adhesive.
Mfr. Model | Container | Strength | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Name | No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Shear, lbs./sq. in. | Peel | Consistency (Viscosity) | Temp. Range, °F | Color | For Joining | Each | |
HighHeat | 8297 | 2 | Stick | 60 min. | 8 hrs. | 900 | Not Rated | Putty (Not Rated) | -20° to 450° | Gray | Metal, Plastic, Rubber, Composites, Masonry | 000000 | 00000 |
PlasticWeld | 8237 | 2 | Stick | 20 min. | 24 hrs. | 900 | Not Rated | Putty (Not Rated) | -20° to 300° | Off-White | Plastic, Rubber, Composites, Masonry | 000000 | 0000 |
To allow time to adjust and position parts, these epoxies remain workable for at least 90 minutes. The strongest and most weather- and chemical-resistant structural adhesives, epoxies work especially well on metals.
The size listed is the combined total of the two parts.
Mfr. Model | Container | Strength | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Name | No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Shear, lbs./sq. in. | Peel | Mix Ratio | Consistency (Viscosity) | Temp. Range, °F | For Joining | Each | |
Original | 50165 | 0.85 | Syringe | 4 hrs. | 24 hrs. | 1,800 | Not Rated | 1:1 | Paste (150,000 cP) | Not Rated to 550° | Metal, Plastic, Rubber, Composites, Glass, Masonry | 000000 | 00000 |
Urethane adhesives are the most flexible, so they bond dissimilar materials and damp vibration.
The size listed is the combined total of the two parts.
Mfr. Model | Container | Strength | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Name | No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Shear, lbs./sq. in. | Peel | Mix Ratio | Consistency (Viscosity) | Temp. Range, °F | Color | For Joining | Each | |
Plastic Bonder | 50139 | 0.85 | Syringe | 15 min. | 30 min. | 1,000 | Not Rated | 1:1 | Thick Liquid (50,000 cP) | -20° to 250° | Black | Metal, Metal to Plastic, Metal to Rubber, Metal to Composites, Plastic, Plastic to Rubber, Plastic to Composites, Plastic to Masonry, Rubber, Rubber to Composites, Rubber to Masonry, Composites, Masonry, Wood | 000000 | 00000 |