Container Type Container Type |
---|
![]() | ![]() |
Aerosol Can | Cartridge |
![]() | ![]() |
Sausage Pack | Tube |
For Use On For Use On |
---|
For Joining For Joining |
---|
Formulation Formulation | Show |
---|
|
Formulation Formulation | Hide |
---|
|
Container Size Container Size |
---|
|
|
Mixing Required Mixing Required |
---|
|
Begins to Harden Begins to Harden |
---|
|
|
|
Cure Type Cure Type |
---|
|
Maximum Temperature Maximum Temperature |
---|
|
Minimum Temperature Minimum Temperature |
---|
|
Adhesive Type Adhesive Type |
---|
|
Clarity Clarity |
---|
|
Elongation Elongation |
---|
|
|
|
Consistency Consistency |
---|
|
Shear Strength Shear Strength |
---|
|
Approximate Coverage Approximate Coverage |
---|
|
Peel Strength Peel Strength |
---|
|
Viscosity Viscosity |
---|
|
More
More
Urethane adhesives are the most flexible, so they bond dissimilar materials and damp vibration.
The size listed is the combined total of the two parts. Dispense adhesives in 10.1-oz. cartridges with a standard caulk gun.
5570 is also known as silane modified polymer.
Container | Strength | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Shear, lbs./sq. in. | Peel | Consistency (Viscosity) | Temp. Range, °F | Color | For Joining | Each | |
5570 | 10.1 | Cartridge | 30 min. | 7 days | 400 | Not Rated | Paste (Not Rated) | -40° to 200° | White | Metal, Metal to Plastic, Metal to Rubber, Metal to Composites, Metal to Glass, Plastic, Plastic to Rubber, Plastic to Composites, Plastic to Glass, Plastic to Masonry, Rubber, Rubber to Composites, Rubber to Glass, Rubber to Masonry, Composites, Glass, Masonry, Wood, Wood to Glass | 00000000 | 000000 |
Spray a thin, uniform coat of adhesive on one or both surfaces, air dry, and then bring together to form strong bonds.
Adhesives that cannot be sold to California exceed local regulatory limits on VOCs (volatile organic compounds).
Container Size, oz. | Approximate Coverage | Inverted Dispensing | Begins to Harden | Reaches Full Strength | Shear Strength | Temp. Range | Color | For Joining | Cannot Be Sold To | Each | |
Adhesives | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
12 | 19 sq. ft. @ 2.5 gm/ft² | No | 1 sec. | 24 hrs. | Not Rated | Not Rated | Beige | Fabric, Foam, Plastic, Rubber | CA | 000000 | 00000 |
Form bonds with twice the strength of our other spray adhesives. Spray a thin, uniform coat of adhesive on one or both surfaces, air dry, and then bring together to adhere.
Container Size, oz. | Approximate Coverage | Inverted Dispensing | Begins to Harden | Reaches Full Strength | Shear Strength | Temp. Range | Color | For Joining | Each | |
Adhesives | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
12 | 19 sq. ft. @ 2.5 gm/ft² | No | 15 sec. | 24 hrs. | Not Rated | Not Rated | White | Masonry, Plastic, Rubber | 0000000 | 000000 |
Bond stone and glass to drywall, treated lumber, and subfloors with these adhesives.
Non-sag adhesives won't drip from vertical and overhead surfaces.
Container | Strength | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Approximate Coverage | Begins to Harden | Reaches Full Strength | Shear, lbs./sq. in | Peel, lbs./in. wd. | Consistency | Temp. Range, °F | For Use Outdoors | For Joining | Choose a Color | Each | |
Adhesives | |||||||||||||
3.7 | Tube | 10 ft. @ 1/4" bead | 4 min. | 72 hrs. | 200 | 45 | Paste | -40° to 150° | No | Ceramic, Composites, Glass, Masonry, Metal, Metal to Composites, Metal to Glass, Metal to Plastic, Metal to Rubber, Plastic, Plastic to Composites, Plastic to Glass, Plastic to Masonry, Plastic to Rubber, Rubber, Rubber to Composites, Rubber to Glass, Rubber to Masonry, Wood, Wood to Glass | Clear | 0000000 | 00000 |
3.7 | Tube | 10 ft. @ 1/4" bead | 4 min. | 72 hrs. | 200 | 45 | Paste | -40° to 150° | Yes | Ceramic, Composites, Glass, Masonry, Metal, Metal to Composites, Metal to Glass, Metal to Plastic, Metal to Rubber, Plastic, Plastic to Composites, Plastic to Glass, Plastic to Masonry, Plastic to Rubber, Rubber, Rubber to Composites, Rubber to Glass, Rubber to Masonry, Wood, Wood to Glass | Clear | 0000000 | 00000 |
10.2 | Cartridge | 30 ft. @ 1/4" bead | 4 min. | 72 hrs. | 200 | 45 | Thick Liquid | -40° to 150° | No | Ceramic, Composites, Glass, Masonry, Metal, Metal to Composites, Metal to Glass, Metal to Plastic, Metal to Rubber, Plastic, Plastic to Composites, Plastic to Glass, Plastic to Masonry, Plastic to Rubber, Rubber, Rubber to Composites, Rubber to Glass, Rubber to Masonry, Wood, Wood to Glass | Black | 0000000 | 00000 |
10.2 | Cartridge | 30 ft. @ 1/4" bead | 4 min. | 72 hrs. | 200 | 45 | Paste | -40° to 150° | No | Ceramic, Composites, Glass, Masonry, Metal, Metal to Composites, Metal to Glass, Metal to Plastic, Metal to Rubber, Plastic, Plastic to Composites, Plastic to Glass, Plastic to Masonry, Plastic to Rubber, Rubber, Rubber to Composites, Rubber to Glass, Rubber to Masonry, Wood, Wood to Glass | Clear | 0000000 | 0000 |
10.2 | Cartridge | 30 ft. @ 1/4" bead | 4 min. | 72 hrs. | 200 | 45 | Paste | -40° to 150° | Yes | Ceramic, Composites, Glass, Masonry, Metal, Metal to Composites, Metal to Glass, Metal to Plastic, Metal to Rubber, Plastic, Plastic to Composites, Plastic to Glass, Plastic to Masonry, Plastic to Rubber, Rubber, Rubber to Composites, Rubber to Glass, Rubber to Masonry, Wood, Wood to Glass | Clear | 0000000 | 00000 |
Non-Sag Adhesives | |||||||||||||
10.2 | Cartridge | 30 ft. @ 1/4" bead | 4 min. | 72 hrs. | 200 | 45 | Paste | -40° to 150° | No | Ceramic, Composites, Glass, Masonry, Metal, Metal to Composites, Metal to Glass, Metal to Plastic, Metal to Rubber, Plastic, Plastic to Composites, Plastic to Glass, Plastic to Masonry, Plastic to Rubber, Rubber, Rubber to Composites, Rubber to Glass, Rubber to Masonry, Wood, Wood to Glass | 000000 | 00000 |
These sealants are non-sagging, so they won't drip from vertical and overhead surfaces.
Elongation and joint compression/expansion tolerance indicate flexibility. For joints between dissimilar materials and in environments with wide temperature fluctuation, choose a sealant with a higher elongation or joint compression/expansion tolerance. For high-wear applications, choose a harder sealant for the most abrasion resistance.
Container | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Tensile Strength, psi | Hardness | Temp. Range, °F | For Joining | Color | Each | |
Sika Sikaflex Hybrid Polymer | |||||||||||||
505 UV | 10.1 | Cartridge | 30 min. | 7 days | 275% | Not Rated | 275 | Medium (Durometer 45A) | -40° to 190° | Metal Metal to Plastic Metal to Rubber Metal to Composites Metal to Glass Plastic Plastic to Rubber Plastic to Composites Plastic to Glass Rubber Rubber to Composites Rubber to Glass Composites Composites to Glass Glass Masonry Wood Wood to Glass | White | 0000000 | 000000 |
Container | Each | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Tensile Strength, psi | Hardness | Temp. Range, °F | For Joining | Choose a Color | 1-11 | 12-Up | |
Hybrid Polymer | |||||||||||||
10.1 | Cartridge | 5 min. | 3 days | 500% | -25% to 25% | 400 | Medium (Durometer 50A) | -40° to 190° | Metal Metal to Plastic Metal to Rubber Metal to Glass Plastic Plastic to Rubber Plastic to Glass Rubber Rubber to Glass Glass Masonry Wood | 0000000 | 00000 | 00000 | |
10.1 | Cartridge | 20 min. | 24 hrs. | 250% | -25% to 25% | 225 | Soft (Durometer 25A) | -75° to 250° | Plastic Plastic to Rubber Plastic to Composites Rubber Rubber to Composites Composites Masonry | Clear | 0000000 | 00000 | 00000 |
10.1 | Cartridge | 60 min. | 3 days | 1,000% | -50% to 50% | 350 | Soft (Durometer 25A) | -40° to 200° | Metal Metal to Plastic Metal to Rubber Metal to Glass Plastic Plastic to Rubber Plastic to Glass Rubber Rubber to Glass Glass Masonry Wood | 0000000 | 0000 | 0000 | |
10.3 | Cartridge | 30 min. | 24 hrs. | 450% | -25% to 25% | 180 | Soft (Durometer 35A) | -40° to 195° | Metal Metal to Plastic Metal to Composites Metal to Glass Plastic Plastic to Composites Plastic to Glass Composites Composites to Glass Glass Masonry Wood Wood to Glass | 0000000 | 0000 | 0000 |
Primer for Sika Sikaflex Polyurethane Sealants (3.4-oz Bottle) | 0000000 | Each | 000000 |
Clear enough to read through, these UV-resistant sealants allow optimal light transmission for use with solar cells and fiber optics. Sealants are non-sagging, so they won't drip from vertical and overhead surfaces.
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. 3M 730 UV is good for use between dissimilar materials and in environments with wide temperature fluctuation.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Tensile Strength, psi | Hardness | Temp. Range, °F | For Joining | Each | |
3M Hybrid Polymer | ||||||||||||
730 UV | 10.3 | Cartridge | 30 min. | 24 hrs. | 300% | Not Rated | 250 | Soft (Durometer 30A) | -40° to 190° | Metal Metal to Plastic Metal to Composites Plastic Plastic to Composites Composites Wood | 0000000 | 000000 |
Hybrid Polymer | ||||||||||||
__ | 10.1 | Cartridge | 10 min. | 3 days | 300% | -25% to 25% | 300 | Medium Soft (Durometer 38A) | -40° to 200° | Metal Wood | 0000000 | 0000 |
Apply these sealants on wet surfaces and in cold temperatures. They’re non-sagging, so they won't drip from vertical and overhead surfaces.
Sealants with 1,000% elongation can be applied through running water.
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. Sealants that are good for joining dissimilar materials also work well in environments with wide temperature fluctuation.
Container | Each | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Temp. Range, °F | For Joining | Choose a Color | 1-11 | 12-Up | |
Hybrid Polymer | ||||||||||||
10 | Cartridge | 5 min. | 14 days | Not Rated | -25% to 25% | Not Rated | -20° to 190° | Metal Metal to Plastic Plastic Asphalt Masonry Wood | White | 0000000 | 00000 | 00000 |
10 | Cartridge | 10 min. | 24 hrs. | Not Rated | -25% to 25% | Not Rated | -65° to 190° | Metal Metal to Plastic Plastic Asphalt Masonry Wood | Clear | 0000000 | 00000 | 0000 |
10 | Cartridge | 8 hrs. | 14 days | 550% | -25% to 25% | Soft (Durometer 22A) | -20° to 200° | Metal Metal to Plastic Metal to Composites Plastic Plastic to Composites Composites Masonry Wood | 000000 | 0000 | 0000 | |
10.3 | Cartridge | 45 min. | 4 days | 1,000% | Not Rated | Soft (Durometer 25A) | -40° to 180° | Metal Plastic Rubber Asphalt Composites Glass Masonry Wood | 000000 | 00000 | 0000 | |
10 | Cartridge | 1 sec. | 5 days | 870% | -25% to 25% | Soft (Durometer 20A) | -40° to 180° | Metal Masonry Wood | Clear | 0000000 | 00000 | 00000 |
10 | Cartridge | 1 sec. | 5 days | 870% | -25% to 25% | Soft (Durometer 25A) | -40° to 180° | Metal Masonry Wood | White | 0000000 | 00000 | 00000 |
Clear enough to read through, this UV-resistant sealant allows optimal light transmission for use with solar cells and fiber optics. Apply it in cold temperatures, on wet surfaces, and even through running water. The sealant is non-sagging, so it won't drip from vertical and overhead surfaces.
Elongation indicates flexibility—the higher the value is, the more a sealant can stretch. This sealant is good for use between dissimilar materials and in environments with wide temperature fluctuation.
Container | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Tensile Strength, psi | Hardness | Application Temp. Range, °F | Temp. Range, °F | For Joining | Each | |
Hybrid Polymer | |||||||||||
10.3 | Cartridge | 45 min. | 4 days | 1,000% | 45 | Soft (Durometer 20A) | 40° to 140° | -40° to 180° | Metal Metal to Plastic Metal to Composites Metal to Glass Plastic Plastic to Composites Plastic to Glass Asphalt Composites Composites to Glass Glass Masonry Wood Wood to Glass | 0000000 | 000000 |
Thinner than non-sagging sealants, this sealant flows easily into cracks and has a smooth finish.
Container | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Tensile Strength, psi | Hardness | Temp. Range, °F | For Joining | Color | Each | |
3M Hybrid Polymer | |||||||||||
2084 | 5 | Tube | 5 min. | 24 hrs. | 25 | Not Rated | -30° to 250° | Metal Metal to Glass Glass Wood | Aluminum | 0000000 | 000000 |
These structural sealants combine the mechanical strength of an adhesive with excellent sealing properties and high flexibility. They’re non-sagging, so they won't drip from vertical and overhead surfaces.
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. For joints between dissimilar materials and in environments with wide temperature fluctuation, choose a sealant with a higher elongation or joint compression/expansion tolerance. For high-wear applications, choose a harder sealant for the most abrasion resistance.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Temp. Range, °F | For Joining | Choose a Color | Each | |
3M Hybrid Polymer | ||||||||||||
760 UV | 9.8 | Cartridge | 30 min. | 24 hrs. | 100% | Not Rated | Medium Hard (Durometer 55A) | -40° to 212° | Metal Metal to Plastic Metal to Rubber Metal to Composites Plastic Plastic to Rubber Plastic to Composites Rubber Rubber to Composites Composites Wood | 00000000 | 000000 | |
760 UV | 20.3 | Sausage Pack | 30 min. | 24 hrs. | 100% | Not Rated | Medium Hard (Durometer 55A) | -40° to 212° | Metal Metal to Plastic Metal to Rubber Metal to Composites Plastic Plastic to Rubber Plastic to Composites Rubber Rubber to Composites Composites Wood | 00000000 | 00000 | |
Loctite® Hybrid Polymer | ||||||||||||
5510 | 10.1 | Cartridge | 24 hrs. | 7 days | 140% | Not Rated | Medium Soft (Durometer 44A) | -40° to 200° | Metal Metal to Plastic Metal to Rubber Metal to Composites Plastic Plastic to Rubber Plastic to Composites Rubber Rubber to Composites Composites Masonry Wood | Clear | 0000000 | 00000 |
5510 | 10.1 | Cartridge | 24 hrs. | 7 days | 140% | Not Rated | Medium Soft (Durometer 44A) | -40° to 200° | Metal Metal to Plastic Metal to Rubber Metal to Composites Plastic Plastic to Rubber Plastic to Composites Rubber Rubber to Composites Composites Masonry Wood | Gray | 00000000 | 00000 |
5510 | 10.1 | Cartridge | 24 hrs. | 7 days | 320% | Not Rated | Medium Soft (Durometer 35A) | -40° to 200° | Metal Metal to Plastic Metal to Rubber Metal to Composites Plastic Plastic to Rubber Plastic to Composites Rubber Rubber to Composites Composites Masonry Wood | White | 00000000 | 00000 |
5510 | 10.1 | Cartridge | 24 hrs. | 7 days | 375% | Not Rated | Medium Soft (Durometer 35A) | -40° to 200° | Metal Plastic Rubber Composites Masonry Wood | Black | 00000000 | 00000 |
Caulk is non-sagging, so it won't drip from vertical and overhead surfaces.
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement a sealant can sustain. Caulk is best suited to joints between similar materials that aren't exposed to wide temperature fluctuation.
Container | Each | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Tensile Strength, psi | Hardness | Temp. Range, °F | Specifications Met | For Joining | Color | 1-11 | 12-Up | |
Hybrid Polymer | ||||||||||||||
5.5 | Tube | 3 days | 3 days | 600% | Not Rated | Not Rated | Not Rated | -20° to 180° | ASTM C920 | Metal, Plastic, Composites, Glass, Masonry, Wood | White | 0000000 | 00000 | 00000 |
10.1 | Cartridge | 3 days | 3 days | 600% | Not Rated | Not Rated | Not Rated | -20° to 180° | ASTM C920 | Metal, Plastic, Composites, Glass, Masonry, Wood | White | 0000000 | 0000 | 0000 |
These non-sagging sealants will not drip while hardening on vertical and overhead surfaces. They’re marine grade, so they stand up to water, corrosion from salt spray, mildew, and UV light.
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain. Sealants that are good for joining dissimilar materials also work well in environments with wide temperature fluctuation.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Mfr. Model No. | Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Temp. Range, °F | For Joining | Color | Each | |
3M Hybrid Polymer | ||||||||||||
4000UV | 3 | Tube | 25 min. | 24 hrs. | 700% | Not Rated | Medium Soft (Durometer 40A) | -40° to 190° | Metal Metal to Composites Composites Wood | White | 00000000 | 000000 |
4000UV | 10 | Cartridge | 25 min. | 24 hrs. | 700% | Not Rated | Medium Soft (Durometer 40A) | -40° to 190° | Metal Metal to Composites Composites Wood | White | 00000000 | 00000 |
4000UV | 20.3 | Sausage Pack | 30 min. | 24 hrs. | 700% | Not Rated | Medium Soft (Durometer 40A) | -40° to 190° | Metal Metal to Plastic Metal to Composites Plastic Plastic to Composites Composites Wood | White | 00000000 | 00000 |
Fix roof leaks in cold and wet conditions. These sealants can even be applied underwater. They're non-sagging, so they won't drip from vertical and overhead surfaces. They are good for use in environments with wide temperature fluctuation.
Elongation indicates flexibility—the higher the value is, the more joint movement a sealant can sustain.
Container | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Tensile Strength, psi | Hardness | Application Temp. Range, °F | Temp. Range, °F | For Joining | Color | Each | |
Hybrid Polymer | ||||||||||||
10 | Cartridge | 30 min. | 24 hrs. | 559% | 235 | Soft (Durometer 33A) | 30° to 120° | -40° to 200° | Metal, Plastic, Rubber, Asphalt, Masonry | Black | 000000 | 00000 |
10 | Cartridge | 60 min. | 24 hrs. | 465% | 115 | Soft (Durometer 19A) | 30° to 120° | -40° to 200° | Metal, Plastic, Rubber, Asphalt, Masonry | White | 000000 | 00000 |
Primer (1-gal. Can) | 0000000 | Each | 000000 |
Seal roof openings around pipes, vents, and chimneys. Use the plastic form to enclose the area around the opening and secure it with the self-tapping screws and bonding sealant. Then fill the form with the self-leveling sealant.
Includes | Begins to Harden | Reaches Full Strength | Elongation | Tensile Strength, psi | Hardness | Application Temp. Range, °F | Temp. Range, °F | For Joining | Color | Each | |
Hybrid Polymer | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
56" Lg. × 2" Ht. PVC Plastic Form Roof Bonding Sealant (10 oz. Cartridge) Self-Leveling Sealant (67 oz. Pouch) Self-Tapping Screws Trowel Tool | 25 min. | 3 days | 217% | 110 | Soft (Durometer 34A) | 30° to 120° | -40° to 200° | Metal, Plastic, Rubber, Asphalt, Composites, Masonry | Black | 000000 | 000000 |
56" Lg. × 4" Ht. PVC Plastic Form Roof Bonding Sealant (10 oz. Cartridge) Self-Leveling Sealant (Two 67 oz. Pouches) Self-Tapping Screws Trowel Tool | 25 min. | 3 days | 217% | 110 | Soft (Durometer 34A) | 30° to 120° | -40° to 200° | Metal, Plastic, Rubber, Asphalt, Composites, Masonry | Black | 000000 | 000000 |
Primer (1-gal. Can) | 0000000 | Each | 000000 |
Apply these sealants on wet surfaces and in cold temperatures. Thinner than non-sagging sealants, these flow easily into cracks and have a smooth finish.
Elongation and joint compression/expansion tolerance indicate flexibility—the higher the values are, the more joint movement sealants can sustain.
Container | For Max. Crack | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Size, oz. | Type | Begins to Harden | Reaches Full Strength | Elongation | Joint Compression/ Expansion Tolerance | Hardness | Wd. | Dp. | Application Temp. Range, °F | Temp. Range, °F | For Joining | Choose a Color | Each | |
Hybrid Polymer | ||||||||||||||
9 | Cartridge | 30 min. | 24 hrs. | Not Rated | -12.5% to 12.5% | Not Rated | 1/2" | 3/8" | 20° to 120° | -65° to 200° | Masonry, Wood | Gray | 0000000 | 00000 |
28 | Cartridge | 45 min. | 48 hrs. | 400% | Not Rated | Soft (Durometer 25A) | 1" | 1" | 35° to 120° | -75° to 300° | Metal, Plastic, Rubber, Asphalt, Composites, Masonry, Wood | 0000000 | 00000 |