The five flux cores allow fast soldering that uses less solder and transmits less heat to the joint. Rosin flux is quick acting with strong cleaning action, but leaves residue that requires flux remover. This solder is electrically conductive.
Material Composition | |||||||
---|---|---|---|---|---|---|---|
Tin | Lead | Silver | Melting Temperature, ° F | Dia. | Wt., lbs. | Each | |
For Joining Brass, Bronze, Copper, Nickel Alloys, Stainless Steel, Steel | |||||||
60% | 40% | __ | 375° | 0.025" | 1 | 000000 | 000000 |
60% | 40% | __ | 375° | 0.032" | 1 | 000000 | 00000 |
60% | 40% | __ | 375° | 0.050" | 1 | 000000 | 00000 |
60% | 40% | __ | 375° | 0.062" | 1 | 000000 | 00000 |
62% | 36% | 2% | 370° | 0.025" | 1 | 0000000 | 000000 |
62% | 36% | 2% | 370° | 0.062" | 1 | 0000000 | 00000 |
63% | 37% | __ | 360° | 0.015" | 1 | 000000 | 00000 |
63% | 37% | __ | 360° | 0.025" | 1 | 000000 | 00000 |
63% | 37% | __ | 360° | 0.050" | 1 | 000000 | 00000 |
63% | 37% | __ | 360° | 0.062" | 1 | 000000 | 00000 |
With five rosin flux cores, this solder joins faster, uses less material, and transmits less heat than single-flux-core solder. Rosin flux is quick acting with a strong cleaning action and is electrically conductive, but leaves residue that requires flux remover. This solder is a safer alternative to leaded solder.
Material Composition | ||||||||
---|---|---|---|---|---|---|---|---|
Tin | Silver | Copper | Lead | Melting Temperature, ° F | Diameter | Weight, lbs. | Each | |
For Joining Brass, Bronze, Copper, Nickel Alloys, Stainless Steel, Steel | ||||||||
96% | 4% | __ | 0% | 470° | 0.032" | 1 | 0000000 | 0000000 |
96% | 4% | __ | 0% | 470° | 0.062" | 1 | 0000000 | 000000 |
96% | 4% | __ | 0% | 470° | 0.093" | 1 | 0000000 | 000000 |
96% | 4% | __ | 0% | 470° | 0.125" | 1 | 0000000 | 000000 |
97% | __ | 3% | 0% | 445° | 0.032" | 1 | 0000000 | 00000 |
97% | __ | 3% | 0% | 445° | 0.062" | 1 | 0000000 | 00000 |
97% | __ | 3% | 0% | 445° | 0.093" | 1 | 0000000 | 00000 |
97% | __ | 3% | 0% | 445° | 0.125" | 1 | 0000000 | 00000 |