Material Material | Show |
|---|
|
System of Measurement System of Measurement |
|---|
|
Hardness Rating Hardness Rating |
|---|
|
Shape Shape |
|---|
 | Sheet and Bar |
 | Rod and Disc |
Aluminum Performance Properties Aluminum PerformanceProperties |
|---|
|
Yield Strength Yield Strength |
|---|
|
Maximum Temperature Maximum Temperature |
|---|
|
Appearance Appearance |
|---|
|
Heat Treatment Heat Treatment |
|---|
|
Fabrication Fabrication |
|---|
|
Minimum Temperature Minimum Temperature |
|---|
|
Heat Treatable Heat Treatable |
|---|
|
Certificate Certificate |
|---|
 | Material Certificate with Traceable Lot Number |
About Aluminum
More
High-Strength 6013 Aluminum Rods
- Yield Strength: 52,000 psi
- Hardness: Brinell 125 (Medium)
- Temper: T8
- Fabrication: Extruded
- Specifications Met: ASTM B211
As the strongest multipurpose aluminum we offer, 6013 aluminum has the same good corrosion resistance, weldability, and machinability as 6061 with increased strength. 6013 is often fabricated into high-stress machine parts. It's comparable to high-strength 7075 aluminum, except 6013 is more corrosion resistant and weldable.
Certificates with a traceable lot number are available for these products. Download certificates from ACTIVITY after your order ships.
| Dia. | Dia. Tolerance | Heat Treatment | Temperature Range, °F | 1 ft. Lg. | 3 ft. Lg. | 6 ft. Lg. | |
| 1" | -0.006" to 0.006" | Hardened | -420° to 400° | 0000000 | |||
| 1 1/4" | -0.006" to 0.006" | Hardened | -420° to 400° | 0000000 | |||
| 1 1/2" | -0.006" to 0.006" | Hardened | -420° to 400° | 0000000 | |||
| 1 3/4" | -0.006" to 0.006" | Hardened | -420° to 400° | 0000000 | |||
| 2" | -0.006" to 0.006" | Hardened | -420° to 400° | 0000000 | |||
| 2 1/2" | -0.006" to 0.006" | Hardened | -420° to 400° | 0000000 |
High-Strength 6013 Aluminum Sheets
- Yield Strength: 50,000 psi
- Hardness: Brinell 120 (Medium)
- Temper: T651
- Fabrication: Hot Rolled
As the strongest multipurpose aluminum we offer, 6013 aluminum has the same good corrosion resistance, weldability, and machinability as 6061 with increased strength. 6013 is often fabricated into high-stress machine parts. It's comparable to high-strength 7075 aluminum, except 6013 is more corrosion resistant and weldable.