About Carbon Steel, Alloy Steel, Spring Steel, and Cast Iron
More
Low-Carbon Steel Balls
- Yield Strength: 44,000 psi
- Hardness: Rockwell C60 (Very Hard)
Low-carbon steel offers excellent weldability. It's widely used for parts that don’t require high strength, such as spacers.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
| Dia. | Dia. Tolerance | Heat Treatment | Mechanical Finish | Pkg. Qty. | Pkg. | |
Mirror-Like | ||||||
|---|---|---|---|---|---|---|
| 1/16" | -0.005" to 0.005" | Case Hardened | Tumbled | 500 | 00000000 | 00000 |
| 3/32" | -0.005" to 0.005" | Case Hardened | Tumbled | 500 | 00000000 | 0000 |
| 1/8" | -0.005" to 0.005" | Case Hardened | Tumbled | 500 | 00000000 | 0000 |
| 5/32" | -0.005" to 0.005" | Case Hardened | Tumbled | 500 | 00000000 | 0000 |
| 3/16" | -0.005" to 0.005" | Case Hardened | Tumbled | 250 | 00000000 | 0000 |
| 7/32" | -0.005" to 0.005" | Case Hardened | Tumbled | 250 | 00000000 | 0000 |
| 1/4" | -0.005" to 0.005" | Case Hardened | Tumbled | 250 | 00000000 | 0000 |
| 9/32" | -0.005" to 0.005" | Case Hardened | Tumbled | 250 | 00000000 | 00000 |
| 5/16" | -0.005" to 0.005" | Case Hardened | Tumbled | 250 | 00000000 | 0000 |
| 11/32" | -0.005" to 0.005" | Case Hardened | Tumbled | 100 | 00000000 | 0000 |
| 3/8" | -0.005" to 0.005" | Case Hardened | Tumbled | 250 | 00000000 | 00000 |
| 7/16" | -0.005" to 0.005" | Case Hardened | Tumbled | 100 | 00000000 | 0000 |
| 1/2" | -0.005" to 0.005" | Case Hardened | Tumbled | 100 | 00000000 | 00000 |
| 9/16" | -0.005" to 0.005" | Case Hardened | Tumbled | 100 | 00000000 | 00000 |
| 5/8" | -0.005" to 0.005" | Case Hardened | Tumbled | 50 | 00000000 | 00000 |
| 3/4" | -0.005" to 0.005" | Case Hardened | Tumbled | 25 | 00000000 | 00000 |
| 7/8" | -0.005" to 0.005" | Case Hardened | Tumbled | 20 | 00000000 | 00000 |
| 1" | -0.005" to 0.005" | Case Hardened | Tumbled | 10 | 00000000 | 00000 |