Determine if aluminum is the right material for you and which alloys will work best.
Multipurpose 6061 Aluminum Sheets and Bars

The most widely used aluminum, 6061 is fabricated into everything from pipe fittings and containers to automotive and aerospace parts. It is strong and corrosion resistant, plus it's easy to machine and weld.
Extruded sheets and bars are formed by a die for close-tolerance widths, then cut to the lengths listed.
Aluminum that meets ASTM B209 or ASTM B221 complies with standards for materials.
Aluminum that meets an SAE AMS standard conforms to the material and process needs of the aerospace industry.
If you don’t see the sheet or bar size you need, please specify dimensions under additional sheet sizes or additional bar lengths.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
- Yield Strength: 35,000 psi
- Hardness: Brinell 95 (Soft)
- Temper: See table
- Fabrication: See table
- Specifications Met: See table
Thick. | Thick. Tolerance | Fabrication | Temper | Heat Treatment | Temp. Range, °F | Specifications Met | Each | |
2" × 48" | ||||||||
---|---|---|---|---|---|---|---|---|
5/8" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | 000000 |
4" × 48" | ||||||||
5/8" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | 000000 |
6" × 6" | ||||||||
5/8" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | 00000 |
6" × 12" | ||||||||
5/8" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | 00000 |
6" × 48" | ||||||||
5/8" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | 000000 |
8" × 8" | ||||||||
5/8" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 0000000 | 00000 |
12" × 48" | ||||||||
5/8" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | 000000 |
- Yield Strength: 35,000 psi
- Hardness: Brinell 95 (Soft)
- Temper: See table
- Fabrication: See table
- Specifications Met: See table
Wd. | Thick. Tolerance | Fabrication | Temper | Heat Treatment | Temp. Range, °F | Specifications Met | 1/2 ft. Lg. | 1 ft. Lg. | 2 ft. Lg. | 3 ft. Lg. | 4 ft. Lg. | 6 ft. Lg. | 8 ft. Lg. | |
5/8" Thick. | ||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
5/8" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 0000000 | |||||||
3/4" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 210° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | |||||||
1" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 0000000 | |||||||
1 1/4" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | |||||||
1 1/2" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 0000000 | |||||||
2" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 0000000 | |||||||
2 1/2" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | |||||||
3" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | |||||||
3 1/2" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 0000000 | |||||||
4" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | |||||||
5" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | |||||||
6" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 210° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | |||||||
8" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 | |||||||
12" | -0.009" to 0.009" | Extruded | T6511 | Hardened | -320° to 300° | ASTM B221, SAE AMS QQ-A-200/8 | 00000000 |
Tight-Tolerance Multipurpose 6061 Aluminum Sheets and Bars

- Yield Strength: 35,000 psi
- Hardness: Brinell 95 (Soft)
- Temper: See table
- Fabrication: See table
- Specifications Met: ASTM B209
These sheets and bars are precision ground either on all six sides or just on the top and bottom. The most widely used aluminum, 6061 is fabricated into everything from pipe fittings and containers to automotive and aerospace parts. It is strong and corrosion resistant, plus it's easy to machine and weld.
Sheets and bars that are precision ground on all sides are consistently flat, square, and parallel on all six sides. They’re also known as blanks and are ready for use in your CNC machine.
Sheets and bars that are precision ground on top and bottom are also known as flat stock.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
Thick. | Thick. Tolerance | Fabrication | Temper | Heat Treatment | Temperature Range, °F | Parallel Tolerance | Flatness Tolerance | Each | |
Precision Ground on All Sides | |||||||||
---|---|---|---|---|---|---|---|---|---|
1/2" x 12" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 000000 |
1" x 12" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 00000 |
2" x 2" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 00000 |
2" x 3" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 00000 |
2" x 4" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 00000 |
2" x 6" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 00000 |
2" x 12" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 0000000 | 00000 |
3" x 3" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 00000 |
3" x 6" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 00000 |
4" x 4" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 00000 |
4" x 6" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 00000 |
4" x 8" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 00000 |
4" x 12" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 0000000 | 00000 |
6" x 6" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 0000000 | 00000 |
6" x 12" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 0000000 | 000000 |
6" x 24" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 000000 |
8" x 8" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 0000000 | 000000 |
8" x 12" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 0000000 | 000000 |
8" x 24" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 000000 |
12" x 12" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 0000000 | 000000 |
12" x 18" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 0000000 | 000000 |
12" x 24" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 0000000 | 000000 |
12" x 36" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 000000 |
24" x 24" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 0000000 | 000000 |
36" x 36" | |||||||||
5/8" | -0.002" to 0.002" | Cold Rolled | T651 | Hardened | -320° to 300° | __ | Not Rated | 00000000 | 00000000 |
Precision Ground on Top and Bottom | |||||||||
2" x 12" | |||||||||
5/8" | -0.002" to 0.002" | Hot Rolled | T651 | Hardened | -320° to 300° | 0.004" | 0.005" | 00000000 | 00000 |
2" x 24" | |||||||||
5/8" | -0.002" to 0.002" | Hot Rolled | T651 | Hardened | -320° to 300° | 0.004" | 0.005" | 00000000 | 000000 |
4" x 12" | |||||||||
5/8" | -0.002" to 0.002" | Hot Rolled | T651 | Hardened | -320° to 300° | 0.004" | 0.005" | 00000000 | 000000 |
4" x 24" | |||||||||
5/8" | -0.002" to 0.002" | Hot Rolled | T651 | Hardened | -320° to 300° | 0.004" | 0.005" | 00000000 | 000000 |
6" x 6" | |||||||||
5/8" | -0.002" to 0.002" | Hot Rolled | T651 | Hardened | -320° to 300° | 0.004" | 0.005" | 0000000 | 000000 |
6" x 12" | |||||||||
5/8" | -0.002" to 0.002" | Hot Rolled | T651 | Hardened | -320° to 300° | 0.004" | 0.005" | 0000000 | 000000 |
6" x 24" | |||||||||
5/8" | -0.002" to 0.002" | Hot Rolled | T651 | Hardened | -320° to 300° | 0.004" | 0.005" | 00000000 | 000000 |
12" x 12" | |||||||||
5/8" | -0.002" to 0.002" | Hot Rolled | T651 | Hardened | -320° to 300° | 0.004" | 0.005" | 0000000 | 000000 |
12" x 18" | |||||||||
5/8" | -0.002" to 0.002" | Hot Rolled | T651 | Hardened | -320° to 300° | 0.004" | 0.005" | 0000000 | 000000 |
12" x 24" | |||||||||
5/8" | -0.002" to 0.002" | Hot Rolled | T651 | Hardened | -320° to 300° | 0.004" | 0.005" | 00000000 | 000000 |
Oversized Multipurpose 6061 Aluminum Sheets

- Yield Strength: 35,000 psi
- Hardness: Brinell 95 (Soft)
- Temper: T651
- Fabrication: Hot Rolled
- Specifications Met: ASTM B209
The thickness is oversized to allow for finishing to exact requirements. The most widely used aluminum, 6061 is fabricated into everything from pipe fittings and containers to automotive and aerospace parts. It is strong and corrosion resistant, plus it's easy to machine and weld.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
Architectural 6063 Aluminum Bars with Rounded Edges

- Yield Strength: 16,000 psi
- Hardness: Brinell 55 (Soft)
- Temper: T5
- Fabrication: Extruded
- Specifications Met: ASTM B221
More corrosion resistant and easier to form than multipurpose 6061 aluminum, 6063 is primarily used for exterior railings, decorative trim, and door frames.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
Architectural 6063 Aluminum Bars

- Yield Strength: 16,000 psi
- Hardness: Brinell 55 (Soft)
- Temper: T5
- Fabrication: Extruded
- Specifications Met: ASTM B221
More corrosion resistant and easier to form than multipurpose 6061 aluminum, 6063 is primarily used for exterior railings, decorative trim, and door frames.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
Wd. | Heat Treatment | Temperature Range, °F | Flatness Tolerance | 4 ft. Lg. | 8 ft. Lg. | |
5/8" Thick. (-0.009" to 0.009" Tolerance) | ||||||
---|---|---|---|---|---|---|
5/8" | Hardened | -320° to 212° | 0.006" per in. of width | 00000000 | ||
1" | Hardened | -320° to 212° | 0.006" per in. of width | 00000000 | ||
1 1/4" | Hardened | -320° to 212° | 0.006" per in. of width | 00000000 | ||
1 1/2" | Hardened | -320° to 212° | 0.006" per in. of width | 00000000 | ||
2" | Hardened | -320° to 212° | 0.006" per in. of width | 00000000 |
High-Strength 2024 Aluminum Sheets and Bars

While 2024 aluminum was initially designed for structural components in aircraft, it's now widely used when a high strength-to-weight ratio is needed, such as for gears, shafts, and fasteners. It offers similar performance to 7075 aluminum, but it’s not as strong.
Cold-drawn bars are formed by a die for close-tolerance widths, then cut to the lengths listed.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
- Yield Strength: 47,000 psi
- Hardness: Brinell 120 (Medium)
- Fabrication: Cold Drawn
- Temper:
1/8" to 3/8" thick. bars: T4
All other sizes: T351 - Specifications Met: ASTM B211
Wd. | Heat Treatment | Temperature Range, °F | 1/2 ft. Lg. | 1 ft. Lg. | 2 ft. Lg. | 3 ft. Lg. | 6 ft. Lg. | |
5/8" Thick. (-0.003" to 0.003" Tolerance) | ||||||||
---|---|---|---|---|---|---|---|---|
5/8" | Hardened | -320° to 300° | 00000000 | |||||
3/4" | Hardened | -320° to 300° | 000000000 | |||||
1" | Hardened | -320° to 300° | 000000000 | |||||
1 1/4" | Hardened | -320° to 300° | 000000000 | |||||
1 1/2" | Hardened | -320° to 300° | 000000000 | |||||
2" | Hardened | -320° to 300° | 000000000 |
Tight-Tolerance High-Strength 7075 Aluminum Sheets and Bars

- Yield Strength: 73,000 psi
- Hardness: Brinell 150 (Medium)
- Temper: T651
- Fabrication: Hot Rolled
- Specifications Met: ASTM B209, SAE AMS-QQ-A-250/12
Choose between sheets and bars that are precision ground on all six sides or just on the top and bottom. Originally developed for aircraft frames, uses for 7075 aluminum now include keys, gears, and other high-stress parts. It is often used as a replacement for 2024 aluminum because it’s stronger and provides similar performance in all other aspects.
Sheets and bars that are precision ground on all sides are consistently flat, square, and parallel on all six sides. They’re also known as blanks and are ready for use in your CNC machine.
Sheets and bars that are precision ground on top and bottom are also known as flat stock.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
Easy-to-Machine 2011 Aluminum Bars

- Yield Strength: 38,000 psi
- Hardness: Brinell 115 (Soft)
- Temper: T3
- Fabrication: Cold Drawn
- Specifications Met: ASTM B211, SAE AMS-QQ-A-225/3
2011 has the best machinability of all the aluminum alloys. It is the most selected aluminum for screws, tube fittings, hose parts, and other items that require extensive machining.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
Easy-to-Machine MIC6 Cast Aluminum Sheets and Bars

- Yield Strength: 15,000 psi
- Hardness: Brinell 65 (Soft)
- Temper: Not Rated
- Fabrication: Cast
MIC6 is cast from a high-strength 7000-series aluminum, then stress relieved to maintain dimensional stability during high-speed machining. Use these sheets and bars for CNC routing tables, assembly jigs, vacuum chucks, and other applications where consistent flatness and tight tolerances are critical.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
Thick. | Thick. Tolerance | Heat Treatment | Flatness Tolerance | Each | |
6" × 6" | |||||
---|---|---|---|---|---|
5/8" | -0.005" to 0.005" | Stress Relieved | 0.015" | 000000000 | 000000 |
6" × 12" | |||||
5/8" | -0.005" to 0.005" | Stress Relieved | 0.015" | 000000000 | 00000 |
6" × 24" | |||||
5/8" | -0.005" to 0.005" | Stress Relieved | 0.015" | 000000000 | 000000 |
8" × 8" | |||||
5/8" | -0.005" to 0.005" | Stress Relieved | 0.015" | 000000000 | 00000 |
12" × 12" | |||||
5/8" | -0.005" to 0.005" | Stress Relieved | 0.015" | 00000000 | 000000 |
12" × 24" | |||||
5/8" | -0.005" to 0.005" | Stress Relieved | 0.015" | 000000000 | 000000 |
12" × 48" | |||||
5/8" | -0.005" to 0.005" | Stress Relieved | 0.015" | 000000000 | 000000 |
18" × 18" | |||||
5/8" | -0.005" to 0.005" | Stress Relieved | 0.015" | 000000000 | 000000 |
24" × 24" | |||||
5/8" | -0.005" to 0.005" | Stress Relieved | 0.015" | 00000000 | 000000 |
24" × 72" | |||||
5/8" | -0.005" to 0.005" | Stress Relieved | 0.015" | 00000000 | 00000000 |
Easy-to-Machine Cast Aluminum for Tool and Jig Plates

Made of 5083 aluminum, these cast tool and jig plates are more corrosion resistant and respond better to anodizing than MIC6. This material is comparable to Alca 5 and ATP 5. Use for CNC routing tables, assembly jigs, vacuum chucks, and other applications where consistent flatness and tight tolerances are critical.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
- Yield Strength: 18,000 psi
- Hardness: Brinell 70 (Soft)
- Temper: O
- Fabrication: Cast
Thick. | Thick. Tolerance | Heat Treatment | Temperature Range, °F | Flatness Tolerance | Each | |
6" × 6" | ||||||
---|---|---|---|---|---|---|
5/8" | -0.005" to 0.005" | Annealed (Softened) | -315° to 250° | 0.005" | 0000000 | 000000 |
6" × 12" | ||||||
5/8" | -0.005" to 0.005" | Annealed (Softened) | -315° to 250° | 0.005" | 0000000 | 00000 |
6" × 24" | ||||||
5/8" | -0.005" to 0.005" | Annealed (Softened) | 70° to 350° | 0.005" | 00000000 | 000000 |
8" × 8" | ||||||
5/8" | -0.005" to 0.005" | Annealed (Softened) | -315° to 250° | 0.005" | 0000000 | 00000 |
12" × 12" | ||||||
5/8" | -0.005" to 0.005" | Annealed (Softened) | 70° to 350° | 0.005" | 00000000 | 000000 |
12" × 24" | ||||||
5/8" | -0.005" to 0.005" | Annealed (Softened) | 70° to 350° | 0.005" | 00000000 | 000000 |
18" × 18" | ||||||
5/8" | -0.005" to 0.005" | Annealed (Softened) | 70° to 350° | 0.005" | 00000000 | 000000 |
24" × 24" | ||||||
5/8" | -0.005" to 0.005" | Annealed (Softened) | 70° to 350° | 0.005" | 00000000 | 000000 |